Double Component Low Viscosity Epoxy Resin Primer with No Solvent Content
Used as a primer before concrete surfaces on the interior areas, cement-based screeds, all Epoxy and Polyurethane coatings.
Used as a bonding element for epoxy-based correction mortars and screeds.
It may be used as final fine coat on floors that are required to be water-proof, non-dusting, and chemically and mechanically resistant in the interior areas.
| Humidity (N.O.) and Temperature | Pedestrian Traffic | Light Traffic | Full Curing |
|---|---|---|---|
| N.O. % 60 +10 °C | 16 hours | 3 days | 10 days |
| N.O. % 60 +20 °C | 13 hours | 2 days | 7 days |
| N.O. % 60 +30 °C | 10 hours | 1 day | 5 days |
Resistant against: Gasoline, beer, cyclohexanol, diesel oil, ethanol 10%, ethylene glycol, glycerine, milk, sodium chloride solution 3-30%, sodium hydroxide 10%, olive oil, paraffin, petroleum, castor oil, silicone oil, turpentine, water and soap.
Partially resistant against: Butanol, methylisobutylketone, perchlorethylene and xylene.
* Discolouration may occur due to the effect of the chemicals. This study is performed at room temperature. High temperature values and/or chemical mixtures may affect chemical strength.
Concrete sub-surfaces shall be clean, dry and free of any foreign material such as dirt, oil, grease, coating and surface curing materials, etc.
Also, they shall be solid and have adequate compressive strength (at least 25 N/mm²), and their tensile strength shall be at least 1,5 N/mm².
The cement sub-surfaces shall be prepared so that a surface with open pores shall be obtained by removing the grout with abrasive equipment.
Weak concrete parts shall be removed from the surface, eyelet holes and holes shall be closed completely. Repairs of sub-surfaces, filling of holes and correction of the surface are made with the mortar obtained by mixing the EPOFLOOR PRIMEL primer with silica sand of 0.1 mm – 0.3 mm thickness.
Concrete or screed surfaces shall be primed and levelled to ensure a smooth surface. The bumps on the surface shall be corrected by abrading. All dust and loose particles shall be removed from the surface prior to application of the product, preferably with a brush and/or vacuum cleaner.
After pouring component B to the component A, it shall be mixed with a 300-400 rpm mixer for about 2-3 minutes until a homogeneous mixture is achieved.
Then, silica sand of 0.1 mm – 0.3 mm and other additives, if required, shall be added and it shall be mixed again until a homogeneous mixture is achieved (about 2-3 minutes). To ensure that the mixture is obtained fully, take the materials to another vessel and mix again for 1 minute. In order to minimize the air-entrainment, avoid mixing excessively. Ensure that the surface moisture content is below 4% and that no dewing shall occur before application.
As primer: EPOFLOOR PRİMEL, shall be applied with a brush, roll, or rake. Ensure that it is applied on whole surface without any holes.
As levelling mortar: Rough surfaces shall be levelled first. Levelling mortar shall be applied with a trowel or rake as per the required thickness.
As Mortar Coating/Repair mortar: Mortar shall be applied properly by using levelling laths, and if necessary, using coating boards, on the primer that is still adhesive. After waiting for a short period of time, surface shall be corrected by compacting it with a trowel or a teflon-coated finishing machine (usually at 20-90 rpm).
Primer:
Fine Levelling Mortar (surface roughness < 1 mm): 1 coat of EPOFLOOR PRIMEL + silica sand (0.1 mm – 0.3 mm)
Screed Mortar/ Repair Mortar: 15 mm – 20 mm coat thickness
| Coating System | Product | Consumption |
|---|---|---|
| Primer | EPOFLOOR PRİMEL | ~ 0,2 kg/m² |
| Fine Levelling Mortar (Surface roughness < 1 mm) |
1 unit of EPOFLOOR PRIMEL in terms of weight + 0.5 unit of silica sand in terms of weight (0.1 mm – 3 mm) |
~ 1,4 kg/m²/mm |
| Mortar Screed (5 mm – 20 mm coat thickness)/ Repair Mortar | 1 unit of EPOFLOOR PRIMEL in terms of weight + 9 units of special silica sand mixture in terms of weight |
~ 2,2 kg/m²/mm |
These values are theoretical and do not include the additional materials required due to surface porosity, profile, differences in levelling and losses.
15 kg Set,
Component A: 10 kg bucket,
Component B: 5 kg bucket
(delivered in pallets or as sling-bags upon request.)
1 Year Shelf Life*
* If stored in its original package without opening the package under dry, frost free conditions
(1 week after opening the package.)
Complies with TS EN 1504-2 / April 2008 standard