Double Component Low Solvent Content Special Epoxy Resin Based Coating Material With Texture
It may be used as final fine coat on floors that are required to be water-proof, non-dusting, and chemically and mechanically resistant. Provides an ideal floor system for schools, workshops, cooling cells, galleries and locker rooms.
| Humidity (N.O.) and Temperature | Pedestrian Traffic | Light Traffic | Full Curing Period |
|---|---|---|---|
| N.O. % 60 +10 °C | 16 hours | 3 days | 10 days |
| N.O. % 60 +20 °C | 13 hours | 2 days | 7 days |
| N.O. % 60 +30 °C | 10 hours | 1 day | 5 days |
Resistant against: Gasoline, beer, cyclohexanol, diesel oil, ethanol 10%, ethylene glycol, glycerine, milk, sodium chloride solution 3-30%, sodium hydroxide 10%, olive oil, paraffin, petroleum, castor oil, silicone oil, turpentine, water and soap.
Partially resistant against: Butanol, ethanol, methylisobutylketone, perchlorethylene and xylene.
* Discolouration may occur due to the effect of the chemicals. This study is performed at room temperature. High temperature values and/or chemical mixtures may affect chemical strength.
Concrete sub-surfaces shall be clean, dry and free of any foreign material such as dirt, oil, grease, coating and surface curing materials, etc.
Also, they shall be solid and have adequate compressive strength (at least 25 N/mm²), and their tensile strength shall be at least 1,5 N/mm².
The cement sub-surfaces shall be prepared so that a surface with open pores shall be obtained by removing the grout with abrasive equipment.
Weak concrete parts shall be removed from the surface, eyelet holes and holes shall be closed completely. Repairs of sub-surfaces, filling of holes and correction of the surface are made with the mortar obtained by mixing the EPOFLOOR PRİMEL primer with silica sand of 0.1 mm – 0.3 mm thickness.
Concrete or screed surfaces shall be primed and levelled to ensure a smooth surface. The bumps on the surface shall be corrected by abrading. All dust and loose particles shall be removed from the surface prior to application of the product, preferably with a brush and/or vacuum cleaner.
Before mixing, Component A shall be stirred mechanically on its own.
After pouring component B to the component A, it shall be mixed with a 300-400 rpm mixer (for about 3 minutes) until a homogeneous mixture is achieved.
Then, silica sand of 0.1 mm – 0.4 mm and other additives, if required, shall be added and it shall be mixed again until a homogeneous mixture is achieved.
To ensure that the mixture is obtained fully, take the materials to another vessel and mix again for 1 minute.
In order to minimize the air-entrainment, avoid mixing excessively.
As Coating: EPOFLOOR COAT TEXT may be applied with a rake or toothed trowel and may be textured with a roll with porocene texture. Orange peel pattern is applied in the final coating (transverse direction).
Protection of Concrete Floors (Painting): Applying with a brush
Coating System:
Primer: EPOFLOOR PRIMEL 0.3 kg/m² – 0.5 kg/m²
Roll Coating: 1 coat of EPOFLOOR COAT TEXT 0.5 kg/m² – 0.7 kg/m² apply for each coat.
These values are theoretical and do not include the additional materials required due to surface porosity, profile, differences in levelling and losses.
Consumption: Approx. 0.5-0.7 kg/m² for coating system
25 kg Set,
Component A: 14 kg bucket,
Component B: 3 kg bucket
(delivered in pallets or as sling-bags upon request.)
1 Year Shelf Life*
* If stored in unopened original packaging, in cool and dry environment, without exposed frost and direct sun light.
Complies with TS EN 1504-2 / April 2008 standard
EPOFLOOR PRİMEL – Primer for concrete and screed surfaces